HIGH STRENGTH COPOLYMEER XTRA
| CONTINOUS IMPROVEMENT IN PRODUCTION AS WELL IN EXTRUSION AND MANUFACTURING OF HSCP YARN AND ROPE RESULTS IN A NEW RANGE OF ROPES. HSCP XTRA ROPES OFFER SUPERIOR FEATURES IN COMPARISON WITH STANDARD POLYPROPYLENE ROPES. HSCP XTRA ROPES ARE MANUFACTURED FROM EXTRUDED HIGH TENACITY COPOLYMEER MELT BLENDED FIBRE BASED 10% POLYESTER AND 90% POLYOLEFINE. THIS PROCESS ENSURES THAT THE ROPES ARE LIGHTWEIGHT AND FLOAT ON WATER DUE TO AN OPTIMALISED PRODUCTION THESE ROPES ARE UP TO 50% STRONGER THAN STANDARD POLYPROPYLENE ROPES. LIKE 100% POLYPROPYLENE ROPES THEY ABSORB VERY LITTLE WATER AND DO NOT SHRINK. THEY REMAIN FLEXIBLE WHEN WET AND DURING USE. |
CONSTRUCTION
ROPES ARE AVAILABLE IN 8-STRAND MULTIPLAIT CONSTRUCTION
COLOUR
STANDARD COLOUR IS YELLOW WITH
BLACK MARKER YARNS
| RELATIVE DENSITY: | 0.91(FLOATS) |
| TEMPERATURE RESISTANCE: | SUITABLE FOR USE DOWN TO -30°C AND UP TO 100°C MELTING POINT 170°C |
| UV RESISTANCE: | FULLY UV STABILISED |
| STRETCH AND RECOVERY : | BREAKING STRETCH OF ABOUT 19% WHEN NEW. RECOVERY AFTER LOAD IS GOOD AND STRETCH IS EVEN |
| FLEXIBILITY: | SUPERIOR HANDLING CHARACTERISTICS FIBRES DO NOT ABSORB WATER AND REMAIN VERY FLEXIBLE WHEN WET |
| CHEMICAL RESISTANCE: | RESISTANCE TO ACIDS AND ALCALIS |
| HSCP XTRA 3- and 8-Strand | ||||||
|---|---|---|---|---|---|---|
| COILS SUPPLIED TO LENGTH WHEN MEASURED UNDER REFERENCE TENSION TO EN 919. | ||||||
| Diameter/ mm | Circumference/ inch | Mass KG/100M |
BL KGF | |||
| 32 | 4 | 49.1 | 20601 | |||
| 36 | 41/2 | 62.1 | 26400 | |||
| 40 | 5 | 76.6 | 32600 | |||
| 44 | 51/2 | 92.6 | 38700 | |||
| 48 | 6 | 110 | 45300 | |||
| 52 | 61/2 | 130 | 53100 | |||
| 56 | 7 | 150 | 60800 | |||
| 60 | 71/2 | 180 | 69700 | |||
| 64 | 8 | 205 | 78500 | |||
| 68 | 81/2 | 233 | 88700 | |||
| 72 | 9 | 261 | 98400 | |||
| 76 | 91/2 | 290 | 110000 | |||
| 80 | 10 | 322 | 121000 | |||
| 88 | 11 | 389 | 140000 | |||
| 96 | 12 | 464 | 164000 | |||
| 104 | 11 | 545 | 190000 | |||