HIGH STRENGTH COPOLYMEER
| HSCP ROPES ARE MANUFACTURED FROM EXTRUDED HIGH TENACITY COPOLYMEER MONOFILAMENT FIBRE BASED MAINLY ON POLYPROPYLENE. THIS PROCESS ENSURES THAT THE ROPES ARE LIGHTWEIGHT AND FLOAT ON WATER. DUE TO AN OPTIMALISED PRODUCTION THESE ROPES ARE UP TO 40% STRONGER THAN STANDARD POLYPROPYLENE ROPES. LIKE 100% POLYPROPYLENE ROPES THEY ABSORB VERY LITTLE WATER AND DO NOT SHRINK. THEY REMAIN FLEXIBLE WHEN WET AND DURING USE. |
CONSTRUCTION AND PUT UP
| RELATIVE DENSITY: | 0.92(FLOATS) |
| TEMPERATURE RESISTANCE: | PERFECT FOR USE BETWEEN -30°C AND +100°C MELTING POINT 170°C |
| UV RESISTANCE: | GOOD STABILISED TO BS 4928 |
| ELONGATION: | BREAKING STRENGTH OF ABOUT 19% WHEN NEW RECOVERY AFTER LOAD IS GOOD AND STRETCH IS EVEN |
| FLEXIBILITY: | SUPERIOR HANDLING CHARACTERISTICS FIBRES DO NOT ABSORB WATER AND REMAIN VERY FLEXIBLE WHEN WET |
| CHEMICAL RESISTANCE: | RESISTANCE TO ACIDS AND ALCALIS |
| HSCP 3- and 8-Strand | ||||||
|---|---|---|---|---|---|---|
| COILS SUPPLIED TO LENGTH WHEN MEASURED UNDER REFERENCE TENSION TO EN 919. | ||||||
| Diameter/ mm | Circumference/ inch | Mass KG/100M | Breaking strength/ DAN |
|||
| 12 | - | 6.5 | 2845 | |||
| 14 | - | 9 | 3831 | |||
| 16 | - | 11.5 | 4817 | |||
| 18 | - | 14.8 | 6185 | |||
| 20 | - | 18 | 7459 | |||
| 22 | - | 22 | 9025 | |||
| 24 | - | 26 | 10301 | |||
| 26 | - | 30.5 | 12361 | |||
| 28 | - | 35.5 | 14225 | |||
| 30 | - | 40.5 | 16088 | |||
| 32 | - | 46 | 18149 | |||
| 34 | - | 52 | 20405 | |||
| 36 | 4 | 58.5 | 22906 | |||
| 38 | 41/2 | 65.5 | 25702 | |||
| 40 | 5 | 72 | 27468 | |||
| 44 | 51/2 | 88 | 33354 | |||
| 48 | 6 | 104 | 38750 | |||
| 52 | 61/2 | 122 | 44636 | |||
| 56 | 7 | 142 | 51012 | |||
| 60 | 71/2 | 163 | 58370 | |||
| 64 | 8 | 185 | 66267 | |||
| 68 | 81/2 | 209 | 74556 | |||
| 72 | 9 | 234 | 82895 | |||
| 76 | 91/2 | 261 | 92214 | |||
| 80 | 10 | 290 | 102024 | |||
| 88 | 11 | 351 | 133416 | |||
| 96 | 12 | 417 | 145188 | |||